电极红铜分类

紫铜类（纯铜）：t2.c1100.c11000.无氧铜tu1.c1020.c10200加磷脱氧铜tp2.c1220.c12200.

黄铜类，铜合金

h96.c2100.c21000.h90.c2200.c22000.h85.c2300.c23000.h80.c2400.c24000.h68a.c2680.  c26200.h65.c2700.c26800.h62.c2720.c27400.

铅黄铜    hpb59-1.c3710.c37800.hpb59-2.c3771.c35300.  hpb60-2.c3604.c36000.hpb63-3.c3560.c34500.hpb63-0.1.c34900.

铝黄铜hai77-2.c6870.c68700.  hai60-1-1.c6782.c67000.hai59-3-2.c67800.hai66-6-3-2.c6872.

锡黄铜hsn62-1.hsn70-1ab.锰黄铜hmn58-2.c67400.hmn57-3-1.铁黄铜hfe59-1-1.c6782.c67820.硅黄铜hsi80-3.c69400.

青铜类：

锡青铜qsn4-3,qsn6.5-0.1.qsn7-0.2.c5212.c52100.qsn6.5-0.4.

铝青铜qai9-2.c61000.qai9-4.qai10-3-1.5.  c6161.c61900.qai10--4-4.c6301.c63000.c63200.

硅青铜qsi3-1.c65500.c65800.qsi1-3.c64700.qsi1.8.  锰青铜qmn5.锆青铜qzr0.2-0.4.铬青铜qcr0.5.c18100.c18200.c18400.qcr1-2.

铬锆铜qcr1-0.15.c18150.  镉青铜qcd1.0.铍青铜qbe1.8.qbe2.0.白铜类：b19.b25.铁白铜bfe10-1--1.b111.c70600.bfe30--1-1.b111.  c71500.

锌白铜bzn15-20.等。

dc53——常用的日本进口冷作模具钢

特性和应用: 高强韧性冷作模具钢，日本大同特殊钢（株）厂家钢号。高温回火后具有高硬度、高韧性，线切割性---。用于精密冷冲压模、拉伸模、搓丝模、冷冲裁模、冲头等10、sm45——普通碳素塑料模具钢（日本钢号s45c）。

dccr12mov——耐磨铬钢（国产）

较cr12钢含碳量低,且加入了mo和v,碳化物不均匀有所---,mo能减轻碳化物偏析并提高淬透性,v能细化晶粒增加韧性.此钢有高淬透性,截面在400mm以下可以完全淬透,在300~400℃仍可保持---的硬度和耐磨性,较cr12有高的韧性，淬火时体积变化小，又有高的耐磨性和---的综合机械性能。所以可以制造截面大，形状复杂，经受较大冲击的各种模具，例如普通拉伸模，冲孔凹模，冲模，落料模，切边模，滚边模，拉丝模，冷挤压模，冷切剪刀，圆锯，标准工具，量具等。该合金具有优良机械加工性能及成屑性能,可迅速缩短零件加工时间等。

二、s136材料常见---、产生原因、解决办法：

s136材料常见---是开裂、裂纹、沙孔、翘皮等---问题。s136模具钢镜面抛光过程中，经常会遇到s136模具钢料纹、麻点、暗团等无法镜面抛光的问题。以上这些问题都会造成模具镜面抛光不可修复的缺陷，只能更换模具钢材，重新生产。造成的损失是无法估量。模具母材:铬铜的导电导热性能、硬度、耐磨抗爆、价格比铍铜模具材料---等特点,已经开始在模具行业代替铍铜作为一般模具材料。

影响s136材料镜面抛光性能的原因和---方法是：

1.模具钢中的杂质(如：非金属夹杂物、气泡、氧化物、---物等)是影响模具钢镜面抛光和研磨时形成和孔洞（俗称沙孔）的主要原因。通过改进炼钢工艺，有效提高模具钢的纯净度，从而提高模具钢的镜面加工性能。